Quantum-splitting oxide-based phosphors, method of producing, and rules for designing the same

ABSTRACT

Strontium and strontium calcium aluminates and lanthanum and lanthanum magnesium borates activated with Pr 3+  and Mn 2+  exhibit characteristics of quantum-splitting phosphors. Improved quantum efficiency may be obtained by further doping with Gd 3+ . Refined rules for designing quantum-splitting phosphors include the requirement of incorporation of Gd 3+  and Mn 2+  in the host lattice for facilitation of energy migration.

CROSS REFERENCE TO RELATED APPLICATIONS

[0001] This patent application is related to patent application Ser. No. ______ (Attorney Docket No. RD-28075), titled “Improved Quantum-Splitting Oxide-Based Phosphors And Method of Producing the Same,” filed on ______.

FEDERAL RESEARCH STATEMENT

[0002] This invention was first conceived or reduced to practice in the performance of work under a contract with the United States Department of Energy, said contract having the contract number of DE-FC26-99FT40632. The United States of America may have certain rights to this invention.

BACKGROUND OF INVENTION

[0003] 1. Field of the Invention

[0004] This invention relates to oxide-based materials that have one application as phosphors. More particularly, the phosphors are oxides doped with Pr³⁺ and Mn²⁺ and exhibit quantum splitting when irradiated with vacuum ultraviolet (“VUV”) radiation. This invention also relates to a method of making and rules for designing such quantum-splitting phosphors.

[0005] 2. Background of the Invention

[0006] The conversion of a single ultraviolet (“UV”) photon into two visible photons with the result that the quantum efficiency of luminescence exceeds unity is termed quantum splitting. Quantum splitting materials are very desirable for use as phosphors for lighting applications, such as fluorescent lamps. A suitable quantum splitting phosphor can, in principle, produce a significantly brighter fluorescent light source due to higher overall luminous output because it can convert to visible light the part of UV radiation that is not absorbed efficiently by traditional phosphors currently used in commercial fluorescent lamps. Quantum splitting has been demonstrated previously in fluoride- and oxide-based materials. A material comprising 0.1% Pr³⁺ in a matrix of YF₃ has been shown to generate more than one visible photon for every absorbed UV photon when excited with radiation having a wavelength of 185 nm. The measured quantum efficiency of this material was 140%, and thus greatly exceeded unity. However, fluoride-based compounds do not have sufficient stability to permit their use as phosphors in fluorescent lamps because they are known to react with mercury vapor that is used in such lamps to provide the UV radiation and form materials that do not exhibit quantum splitting. In addition, producing fluoride-based materials presents a great practical challenge because it involves the use of large quantities of highly reactive and toxic fluorine-based materials.

[0007] The applicants recently disclosed oxide-based quantum splitting materials. U.S. Pat. No. 5,552,082 discloses a lanthanum magnesium borate activated with Pr³⁺ ion. U.S. Pat. No. 5,571,4151 discloses a strontium magnesium aluminate activated with Pr³⁺ ion and charge compensated with Mg²⁺ ion. Emission spectra of these materials exhibit a large peak at about 405 nm which is characteristic of quantum splitting.

[0008] However, these materials still exhibit a considerable emission in the UV wavelength range of less than 350 nm. This part of the emission reduces the overall visible light output that otherwise can be higher. Therefore, it is desirable to provide oxide-based quantum-splitting phosphors that have higher quantum efficiency in the visible range than the prior-art quantum splitting materials. It is also desirable to provide more energy-efficient light sources using quantum-splitting phosphors having higher quantum efficiency. It is further desirable to provide method for making and rules for guiding the design of materials having high quantum-splitting capability.

SUMMARY OF INVENTION

[0009] The present invention provides oxide-based phosphors doped with at least Pr³⁺ and Mn²⁺ ions, which phosphors exhibit quantum splitting when irradiated with VUV radiation. VUV radiation as used herein is radiation having wavelength shorter than about 215 nm. The oxide phosphors of the present invention are oxides of aluminum or boron having positive counterions selected from Group IIA and IIIA of the Periodic Table. The phosphors of the present invention may be used in mercury vapor discharge lamps to provide energy-efficient light sources.

[0010] In one aspect of the present invention, the oxide-based phosphors are strontium aluminates in which strontium may be partially or completely substituted with calcium and which are doped with at least Pr³⁺ and Mn²⁺. Such oxide-based phosphors of the present invention have a composition represented by Sr_(1−x)Ca_(x)Al₁₂O₁₉:Pr³⁺,Mn²⁺ where 0≦x≦1. In this convention, the elements following the colons are the activators in the phosphors.

[0011] In another aspect of the present invention, the oxide-based phosphors are also doped with Gd³⁺ in addition to Pr³⁺ and Mn²⁺.

[0012] In still another aspect of the present invention, the oxide-based phosphors are doped with La³⁺ and Mg²⁺ ions for charge compensation and for minimization of the number of vacancies in the lattice.

[0013] In another aspect of the present invention, the oxide-based phosphors are lanthanum borate activated with Pr³⁺ and Mn²⁺ in which lanthanum is partially substituted by gadolinium. In addition, the borate phosphors may be doped with Mg²⁺. Such borate phosphors of the present invention have compositions represented by La_(1−x−y−z)Gd_(x)Pr_(y)Mn_(z)B₃O₆ where x is in the range from about 0.005 to about 0.99, y is in the range from about 0.005 to about 0.1, z is in the range from about 0.005 to about 0.5, and x+y+z<1. Another borate phosphor of the present invention has a formula of La_(1−x−y)Gd_(x)Pr_(y)Mg_(1−z)Mn_(z)B₅O₁₀ where x is in the range from about 0.005 to about 0.995, y is in the range from about 0.005 to about 0.1, z is in the range from about 0.005 to about 0.5, and x+y<1.

[0014] The present invention also provides a method of making improved quantum-splitting aluminate or borate phosphors. The aluminate phosphors have a formula of Sr_(1−x)Ca_(x)Al₁₂O₁₉:Pr³⁺,Mn²⁺ or Sr_(1−x)Ca_(x)Al₁₂O₁₉:Pr³⁺,Mn²⁺,A; where 0≦x≦1, and A is selected from the group consisting of Gd³⁺, La³⁺, Mg²⁺, and combinations thereof. The borate phosphors have a formula of La_(1−x−y−z.)Gd_(x)Pr_(y)Mn_(z)B₃O₆ where x is in the range from about 0.005 to about 0.99, y is in the range from about 0.005 to about 0.1, z is in the range from about 0.005 to about 0.5, and x+y+z<1 or a formula of La_(1−x−y−z)Gd_(x)Pr_(y)Mg_(1−z)Mn_(z)B₅O₁₀ where x is in the range from about 0.005 to about 0.995, y is in the range from about 0.005 to about 0.1, z is in the range from about 0.005 to about 0.5, and x+y<1. The method comprises the steps of selecting a desired final composition of the phosphor; mixing together oxygen-containing compounds of praseodymium and manganese, and materials selected from the group consisting of oxygen-containing compounds of strontium, calcium, aluminum, boron, gadolinium, lanthanum, and magnesium so as to achieve the desired final composition; forming a substantially homogeneous mixture of the selected compounds; and firing the substantially homogeneous mixture in a non-oxidizing atmosphere at a temperature and for a time sufficient to result in the desired composition and to maintain the praseodymium ion in the 3+ valence state and manganese ion in the 2+ valence state.

[0015] Other benefits of this invention may become evident upon a perusal of the description and appended claims together with the attached drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

[0016]FIG. 1 is a diagram showing energy levels of Pr³⁺, Gd³⁺, and Mn²⁺ ions.

[0017]FIG. 2 shows an emission spectrum of strontium aluminate activated by Pr³⁺, Gd³⁺, and Mn²⁺ and an excitation spectrum of Mn²⁺ showing energy absorption by Gd³⁺ and energy transfer between Gd³⁺ and Mn²⁺.

[0018]FIG. 3 shows an excitation spectrum of Gd³⁺ in a strontium aluminate activated by Pr³⁺, Gd³⁺, and Mn²⁺.

[0019]FIG. 4 is a schematic illustration of a lamp incorporating a phosphor of the present invention.

DETAILED DESCRIPTION

[0020] In general, the present invention provides oxide-based phosphors activated with Pr³⁺ and Mn²⁺. More particularly, the phosphors are strontium aluminate and lanthanum borate phosphors activated with at least Pr³⁺ and Mn²⁺ ions. The doping level for Pr³⁺ and Mn²⁺ are typically in the range from about 0.005 to about 0.1 and from about 0.005 to about 0.5, respectively. In addition, the strontium ions of the aluminate phosphors of the present invention may be substituted partially or completely by calcium. In one preferred embodiment of the present invention, the aluminate phosphor is further doped with gadolinium. The preferred doping level for Gd³⁺ is in the range from about 0.005 to about 0.995 depending on the host lattice. In another preferred embodiment of the present invention, the aluminate phosphor is further doped with La³⁺ and Mg²⁺ at sufficient levels for charge compensation and for minimization of the number of vacancies in the lattice. Thus, the aluminate phosphors have a formula of Sr_(1−x)Ca_(x)Al₁₂O₁₉:Pr³⁺,Mn²⁺ or Sr_(1−x)Ca_(x)Al₁₂O₁₉:Pr³⁺,Mn²⁺,A; where 0≦x≦1 and A is at least one selected from the group consisting of Gd³⁺, La³⁺, Mg²⁺, and combinations thereof.

[0021] In another preferred embodiment of the present invention, the oxide-based phosphor is a lanthanum borate activated with at least Pr³⁺ and Mn²⁺ in which lanthanum is partially substituted by gadolinium. In addition, the borate phosphor may be doped with Mg²⁺. The lanthanum borate phosphors of the present invention have a formula of La_(1−x−y−z)Gd_(x)Pr_(y)Mn_(z)B₃O₆ where x is in the range from about 0.005 to about 0.5, y is in the range from about 0.005 to about 0.1, z is in the range from about 0.005 to about 0.5, and x+y<1. The applicants have observed that the strontium aluminate phosphors of the present invention exhibit quantum splitting. A lanthanum borate has been shown to possess quantum-splitting capability (U.S. Pat. No. 5,552,082). The lanthanum borates of the present invention also are expected to be quantum splitting and have a higher quantum efficiency than the lanthanum borate of the prior art because a substantial amount of radiation emitted by the Pr³⁺ ion in the UV range can be transferred through Gd³⁺ ions to Mn²⁺ ions where it is re-emitted as visible light.

[0022] In general, emission spectra of materials exhibiting quantum-splitting capability show a characteristic peak at about 405 nm, which peak is a result of the first visible photon emitted as the excited Pr³⁺ ion radiatively decays from the ¹S₀ energy level to the ¹I₆ energy level. Thus, an examination of the intensity-versus-wavelength spectrum provides a convenient way of determining whether a material would be quantum splitting, as opposed to using the more time-consuming measurement of quantum efficiency.

[0023] Without limitation, the quantum-splitting behavior of phosphors is attributed to the VUV excitation of the Pr³⁺ ion within the oxide lattice. Therefore, oxides of the present invention should be processed so as to maintain praseodymium as Pr³⁺ ion within the oxide lattice.

[0024]FIG. 1 shows the energy levels of Pr³⁺ Gd³⁺, and Mn²⁺ ions. Although the applicants do not wish to be bound by any particular theory, it is believed that the quantum-splitting phosphors of the present invention offer higher quantum efficiency than other quantum-splitting phosphors of the prior art because of two reasons. First, any Pr³⁺ ions that non-radiatively relax from the ³P₀ energy level to the ¹D₂ energy level transfer their energy to Mn²⁺ ions, which in turn emit a visible photon. Second, the transitions from the ¹S₀ energy level of the Pr³⁺ ion in the UV range (i.e., mainly ¹S₀→¹G₄ and ¹S₀ ³F₄) are converted to visible light by a process consisting of successive steps of cross-relaxation with Gd³⁺ ions, energy migration across the Gd³⁺ sublattice, trapping of that energy by Mn²⁺ ions, and emission of visible photon from the excited Mn²⁺ ions. For simplicity, FIG. 1 shows the energy migration over only two Gd³⁺ ions, but it should be appreciated that, in reality, the energy migration may occur over many Gd³⁺ ions.

EXAMPLE

[0025] A phosphor having the composition of (Sr_(0.65)Gd_(0.30)Pr_(0.05))(Al_(11.65)Mn_(0.1)Mg_(0.25))O₁₉ was produced and tested to show quantum-splitting capability.

[0026] The following amounts of strontium, gadolinium, praseodymium, aluminum, manganese, magnesium compounds were mixed together thoroughly:

[0027] [t1]

[0028] 3.885 g SrCO₃

[0029] 2.201 g Gd₂O₃

[0030] 0.345 g Pr₆O₁₁

[0031] 24.043 g Al₂O₃

[0032] 0.465 g MnCO₃

[0033] 0.408 g MgO

[0034] The mixture was fired at 1400° C. for 6 hours in an atmosphere generated by reactions products of a coconut charcoal and volatized compounds of the decomposition of the above carbonates and oxides. Then the fired material was reblended and fired at 1100° C. for 6 hours in an atmosphere of 1% (by volume) hydrogen in nitrogen to yield the final phosphor.

[0035]FIG. 2 shows the emission spectrum of this phosphor (dotted line) upon being excited by VUV radiation at a wavelength of 205 nm. Superimposed on this emission spectrum is the excitation spectrum (solid line) showing a large absorption by Gd³⁺ at about 272-278 nm. This energy is then transferred between the Gd³⁺ and Mn²⁺ ions and subsequently emitted as a visible photon as evidenced by the large peak at about 525 nm. FIG. 3 shows the excitation spectrum of Gd³⁺ ion in the above strontium aluminate phosphor of the present invention. This spectrum shows the large absorption of energy at about 272-278 nm. This peaks substantially coincides with an emission from the radiative decay ¹S₀→¹G₄ of the Pr³⁺ ion. Therefore, this part of the UV emission from the Pr³⁺ ion is converted to visible light with the assistance of the Gd³⁺ ion in the phosphor of the present invention, lending to higher quantum efficiency; i.e., a more efficient use of energy.

[0036] From the foregoing discussion, a set of rules may be established for designing quantum-splitting phosphors. It is recognized here that: (1) the Pr³⁺ ion still must excited into the 4f5d energy band and (2) the excited Pr³⁺ must decay into the ¹S₀ energy level. Therefore, the Pr³⁺ energy position of its 4f5d band must be located above the ¹S₀ state. However, the 4f5d energy band should not be substantially higher than the ¹S₀ level so to minimize the loss of energy through the non-radiative decay from the 4f5d band to the ¹S₀ level. Other rules that are set forth in U.S. Pat. No. 5,788,884 must still hold for an efficient quantum-splitting phosphor. For example, the Pr³⁺ should occupy a site in the host lattice that results in symmetry so that maximum quantum efficiency may be generated by the phosphor. The Pr³⁺-to-oxygen bond distance must exceed about 0.256 nm for quantum splitting to occur. The host lattice must have a band gap greater than about 5 eV so that the excited electrons of the activator are not lost into the conduction band of the host lattice. The present invention further refines the rules to include the necessity to have (1) a substantial amount of gadolinium in the lattice to allow for a significant energy migration among the Gd³⁺ ions and (2) Mn²⁺ codopant to trap energy migrating from Gd³⁺ ions and convert that energy into visible light.

[0037] A quantum-splitting phosphor of the present invention is made in a process comprising the steps of: (1) selecting the desired final composition of the phosphor such that the phosphor is activated by at least praseodymium and manganese; (2) mixing together oxygen-containing compounds of praseodymium and manganese and materials selected from the group consisting of oxygen-containing compounds of strontium, calcium, aluminum, boron, gadolinium, lanthanum, and magnesium in quantities so as to achieve the desired final composition of the phosphor; (3) forming a substantially homogeneous mixture of the selected compounds; and (4) firing the substantially homogeneous mixture in a non-oxidizing atmosphere at a temperature and for a time sufficient to result in the desired final composition and to maintain the praseodymium ion in the 3+ valence state and the manganese ion in the 2+ valence state. The oxygen-containing compounds used in the process may be selected from the group consisting of oxides, carbonates, nitrates, sulfates, oxalates, and combinations thereof. The oxygen-containing compounds may be in the hydrated or non-hydrated form. In a preferred embodiment, the non-oxidizing atmosphere is generated from materials selected from the group consisting of carbon monoxide, carbon dioxide, hydrogen, nitrogen, ammonia, hydrazine, amines, and combinations thereof. The firing may be done in any suitable high-temperature equipment in either a batch-wise of a continuous process. The firing may be done isothermally. Alternatively, the process temperature may be ramped from ambient temperature to and then held at the firing temperature. The firing temperature is in the range from about 1000° C. to about 2000° C., preferably from about 1200° C. to about 1700° C., more preferably from about 1400° C. to about 1600° C. The firing time should be sufficiently long to convert the mixture to the final desired composition. This time also depends on the quantity of materials being processed and the rate and quantity of non-oxidizing materials conducted through the firing equipment to provide the non-oxidizing atmosphere. A typical firing time is less than 10 hours.

[0038] A phosphor of the present invention characterized by quantum-splitting behavior in VUV radiation and stability with regard to an environment in a mercury discharge device may be utilized as a phosphor in a fluorescent lamp. FIG. 4 shows a lamp 50 comprising an evacuated housing 60, a VUV radiation generating means 70 located within housing 60, and a phosphor 80 located within housing 60 and adapted to be excited by VUV radiation. In a preferred embodiment, lamp 50 is a fluorescent lamp and evacuated housing 60 comprises an evacuated glass tube and associated end caps 62. VUV generating means 70 is a combination of mercury vapor and means for generating high-energy electrons to create a mercury vapor discharge to excite the phosphor. The means for generating high-energy electrons may be a filament of a metal having a low work function, such as tungsten, or such a filament coated with alkali earth metal oxides as are known in the art. The filament is coupled to a high-voltage source to generate electrons from the surface thereof. A quantum-splitting phosphor of the present invention may be used in combination with other conventional phosphors used in fluorescent lighting technology. For example, a quantum-splitting phosphor of the present invention may be combined with conventional red-emitting and blue-emitting phosphors to produce white light from a mercury discharge lamp. Since the quantum-splitting phosphor of the present invention is transparent to the mercury 254-nm emission line, it may be coated on top of the conventional phosphor layer in the lamp housing so to absorb substantially the mercury 185-nm emission line.

[0039] While specified preferred embodiments of the present invention have been described in the foregoing, it will be appreciated by those skilled in the art that many modifications, substitutions, or variations may be made thereto without departing from the spirit and scope of the invention as defined in the appended claims. 

1. An oxide-based quantum-splitting phosphor comprising an oxide of an element selected from the group consisting of aluminum and boron, at least one positive counterion selected from the group consisting of strontium, calcium, and magnesium; said oxide being doped with Pr³⁺ and Mn²⁺ ions; said phosphor exhibiting a quantum-splitting behavior when irradiated by VUV radiation.
 2. The oxide-based quantum-splitting phosphor of claim 1 further doped with Gd³⁺ ion.
 3. The oxide-based quantum-splitting phosphor of claim 1 having a formula Sr_(1−x)Ca_(x)Al₁₂O₁₉:Pr³⁺,Mn²⁺ where 0≦x≦1.
 4. The oxide-based quantum-splitting phosphor of claim 1 having a formula Sr_(1−x)Ca_(x)Al₁₂O₁₉:Pr³⁺,Mn²⁺, A where 0≦x≦1 and A is at least one selected from the group consisting of La³⁺ and Mg²⁺.
 5. The oxide-based quantum-splitting phosphor of claim 4 wherein Pr³⁺ is present at a level from about 0.005 to about 0.1 mole fraction.
 6. The oxide-based quantum-splitting phosphor of claim 4 wherein Mn²⁺ is present at a level from about 0.005 to about 0.5 mole fraction.
 7. The oxide-based quantum-splitting phosphor of claim 4 further doped with Gd³⁺ ion.
 8. The oxide-based quantum-splitting phosphor of claim 7 wherein Gd³⁺ is present at a level from about 0.005 to about 0.5 mole fraction.
 9. The oxide-based quantum-splitting phosphor of claim 1 having a formula La_(1−x−y−z)Gd_(x)Pr_(y)Mn_(z)B₃O₆ where x is in a range from about 0.005 to about 0.99, y is in a range from about 0.05 to about 0.1, z is a range from about 0.005 to about 0.5; and x+y+z<1.
 10. The oxide-based quantum-splitting phosphor of claim 1 having a formula La_(1−x−y)Gd_(x)Pr_(y)Mg_(1−z)Mn_(z)B₅O₁₀ where x is in a range from about 0.005 to about 0.995, y is in a range from about 0.05 to about 0.1, z is a range from about 0.005 to about 0.5; and x+y<1.
 11. A method of making a quantum-splitting phosphor, said method comprising the steps of: (1) selecting a desired final composition of said phosphor such that said phosphor is activated by at least praseodymium and manganese ions; (2) mixing together oxygen-containing compounds of praseodymium and manganese and materials selected from the group consisting of oxygen-containing compounds of strontium, calcium, aluminum, boron, gadolinium, lanthanum, and magnesium in quantities so as to achieve said desired final composition of said phosphor; (3) forming a substantially homogeneous mixture of said oxygen-containing compounds; and (4) firing said substantially homogeneous mixture in a non-oxidizing atmosphere at a temperature and for a time sufficient to result in said desired final composition and to maintain substantially all of said praseodymium ions in a 3+ valence state and said manganese ions in a 2+ valence state.
 12. The method of claim 11 wherein said non-oxidizing atmosphere is generated from materials selected from the group consisting of carbon monoxide, carbon dioxide, hydrogen, nitrogen, ammonia, hydrazine, amines, and mixtures thereof.
 13. The method of claim 11 wherein said firing is done isothermally at a temperature from about 500° C. to about 2000° C.
 14. The method of claim 13 wherein said temperature is preferably in a range from about 900° C. to about 1700° C., more preferably from about 1000° C. to about 1600° C., and most preferably from about 1400° C. to about 1600° C.
 15. The method of claim 14 wherein said firing continues for a time sufficient to convert said substantially homogeneous mixture to said desired final composition.
 16. The method of claim 11 wherein said firing is done while said temperature is ramped from ambient to an end temperature in a range from about 1600° C. to about 1700° C.
 17. The method of claim 16 wherein said firing continues for a time sufficient to convert said substantially homogeneous mixture to said desired final composition.
 18. The method of claim 11 wherein said oxygen-containing compounds are selected from the group consisting of oxides, carbonates, nitrates, sulfates, acetates, citrates, oxalates, and combinations thereof.
 19. The method of claim 18 wherein said oxygen-containing compounds are selected from the group consisting of compounds in a hydrated, a non-hydrated form, and combinations thereof.
 20. A method for designing quantum-splitting phosphors in which a host lattice is activated by at least Pr³⁺ and Mn²⁺ ions, said method comprising: ensuring that Pr³⁺ is incorporated in said host such that a 4f5d band of said Pr³⁺ is located above a ¹S₀ state of said Pr³⁺; ensuring that said 4f5d band and said ¹S₀ state are positioned below a conduction band of said host where said Pr³⁺ is incorporated in a lattice having a band gap greater than about 5 eV; ensuring that a site symmetry of said host lattice for said Pr³⁺ has been chosen having an effective crystal field strength and an effective Pr³⁺-to-host lattice bond distance; and selecting a sufficient amount of Mn²⁺ to incorporate in said host lattice to convert a part of radiation emitted by Pr³⁺ in a UV range to visible light.
 21. The method of designing quantum-splitting phosphors of claim 20 further comprising selecting a sufficient amount of Gd³⁺ to incorporate in said host lattice to transfer energy of radiation emitted by Pr³⁺ in a UV range to Mn2+.
 22. The method for designing quantum-splitting phosphors of claim 20 wherein said host lattice is an oxide host lattice.
 23. The method of designing quantum-splitting phosphors of claim 22 wherein said oxide host lattice is selected from the group consisting of aluminates and borates.
 24. The method for designing quantum-splitting phosphors of claim 23 wherein said oxide host lattice has a Pr³⁺-to-oxygen bond distance greater than about 0.256 nm.
 25. The method for designing quantum-splitting phosphors of claim 20 wherein said site symmetry for Pr³⁺ in said host lattice is selected so maximum quantum efficiency is obtained from said phosphor.
 26. A light source comprising an evacuated housing; a VUV radiation source located within said housing; and a phosphor located within said housing and adapted to be excited by said VUV radiation source; said phosphor comprising an oxide-based quantum-splitting phosphor which comprises an oxide of an element selected from the group consisting of aluminum and boron, at least one positive counterion selected from the group consisting of strontium, calcium, lanthanum, and magnesium; said oxide being doped with Pr³⁺ and Mn²⁺ ions; said phosphor exhibiting a quantum-splitting behavior when irradiated by said VUV radiation.
 27. The light source of claim 26 wherein said quantum-splitting phosphor has a formula Sr_(1−x)Ca_(x)Al₁₂O₁₉:Pr³⁺, Mn²⁺ where 0≦x≦1.
 28. The light source of claim 27 wherein said phosphor is further doped with Gd3+
 29. The light source of claim 26 wherein said quantum-splitting phosphor has a formula Sr_(1−x)Ca_(x)Al₁₂O₁₉:Pr³⁺, Mn²⁺, A where 0≦x≦1 and A is selected from the group consisting of La³⁺ and Mg²⁺.
 30. The light source of claim 26 wherein said phosphor has a formula La_(1−x−y−z)Gd_(x)Pr_(y)Mn_(z)B₃O₆ where x is in a range from about 0.005 to about 0.99, y is in a range from about 0.05 to about 0.1, z is in a range from about 0.005 to about 0.5; and x+y+z<1.
 31. The light source of claim 26 wherein said phosphor has a formula La_(1−x−y)Gd_(x)Pr_(y)Mg_(1−z)Mn_(z)B₅O₁₀ where x is in a range from about 0.005 to about 0.995, y is in a range from about 0.05 to about 0.1, z is in a range from about 0.005 to about 0.5; and x+y<1.
 32. The light source of claim 26 further comprising phosphors that emit red and blue visible radiation when excited by UV radiation
 33. The light source of claim 32 wherein light emitted from said light source is white light. 